Abstract
•Probing resistive switching in hafnium dioxide (HfO2) and aluminum oxide (Al2O3) bilayered stacks using in-situ transmission electron microscopy.•Conductance of the HfO2/Al2O3 stack changes gradually upon electrical stressing which is related to the formation of extended nanoscale physical defects at the HfO2/Al2O3 interface and the migration and re-crystallization of Al into the oxide bulk.•Two competing physical mechanisms exist - including redistribution of oxygen ions and the migration of Al species during the switching process.•Low diffusion barrier of the active Al electrode causes severe Al migration in the bi-layered oxides leading to the device to fail in resetting.
In this work, we investigate the resistive switching in hafnium dioxide (HfO2) and aluminum oxide (Al2O3) bilayered stacks using in-situ transmission electron microscopy and X-ray energy dispersive spectroscopy. Conductance of the HfO2/Al2O3 stack changes gradually upon electrical stressing which is related to the formation of extended nanoscale physical defects at the HfO2/Al2O3 interface and the migration and re-crystallization of Al into the oxide bulk. The results suggest two competing physical mechanisms including the redistribution of oxygen ions and the migration of Al species from the Al electrode during the switching process. While the HfO2/Al2O3 bilayered stack appears to be a good candidate for RRAM technology, the low diffusion barrier of the active Al electrode causes severe Al migration in the bi-layered oxides leading to the device to fail in resetting, and thereby, largely limiting the overall switching performance and material reliability.
[Display omitted]