Abstract
The unlubricated wear of 10.3% porosity sintered medium-carbon and 12.8% porosity sintered low-alloy steels was investigated under different sliding conditions. Their wear characteristics were found to be similar to their non-sintered counterparts. Within this range of sliding conditions, both mild-oxidational and delamination wear took place, with the former dominating the wear processes. The oxide debris produced changed with the applied load: switching from a low-temperature oxide to a high-temperature one at higher loads. The wear rates agreed reasonably well with Archard's law and with data from other sources, suggesting that Archard's law can account for the wear rates produced by both mild-oxidational wear and delamination wear. This agreement also suggests that within the range of porosites investigated an overall framework can be established in the unlubricated wear of both sintered and non-sintered steels.